LOCTITE 1373435 HYSOL 11C ADHÉSIF ÉPOXY BICOMPOSANT À USAGE GÉNÉRAL, TROUSSE DE 4 OZ, NOIR/VERT, 72 H DE DURCISSEMENT
- GLD# HEN-100235
- MFG# 1373435
- UPC 079340439634
Min. Order Qty 1
Description
Colle époxy Loctite, usage général en 2 parties, gamme : Hysol 11c, kit contenant, contenant de 4 oz, composition : une partie : noir de carbone résine époxy ; partie b : talc, résine époxy/durcisseur, quartz (sio2), diéthylènetriamine 4,4-isopropylidènediphénol, silane substitué, pipérazine substituée, >= 20 min dautonomie, durcissement 72 h, noir/vert, 250 deg f, 2.5 :1 rapport de mélange, 0.05 g/l partie a, 0.57 g/l cov partie b, à utiliser sur : métal, plastique et bois
Specifications
| Color | Gray/White |
|---|---|
| UNSPSC | 31201601 |
| Application | Filling Mild Steel and Forming Molds |
| Base Type | Epoxy |
| Container Size | 25 lb |
| Flash Point | >93 deg C |
| Temperature Rating | -30 to 105 deg C |
| Type | 2-Part |
| VOC Content | <10 g/L |
| Composition | Part A: Diiron Trioxide, Epoxy Resin, Calcium Carbonate, Neopentyl Glycol Diglycidyl Ether, Manganese ; Part B:Amine Adduct, Aliphatic Amine Adduct, Triethylenetetramine, Substituted Piperazine, Silicon Dioxide, Aliphatic Amine, 4,4'-Isopropylidenedipheno |
| Container Type | Pail |
| Curing Time | 6 hr |
| Form | Paste |
| Specific Gravity | Part A: 2.6/Part B: 1.5 |
| Series | EA 3471 |
| Application Time | 30 min |
| Coverage | 278 sq-cm at 6 mm THK/0.45 kg |
| Mixing Ratio | 2.5:1 By Volume/6.25:1 By Weight |
| Odor/Scent | Part A: Slight/Musty, Part B: Ammoniacal |
| Shear Strength | 1395 psi |
| Tensile Strength | 4900 psi |
| Applicable Materials | Aluminum, Bronze, Cast Iron, Concrete, Copper, Stainless Steel, Steel |
Features
- Steel putty is a non-slumping, two-part, steel-filled putty
- Will not sag or shrink
- Rebuilds worn parts fast limits downtime
- High steel content cures to a metal-like finish
- Superior adhesion bonds well to all metal substrates
- D 85 shore hardness
- 35 to 40 gel time at 21 deg C
- Epoxy resin part A, epoxy hardener part B