LOCTITE 398455 HYSOL CHAQUE 608 ADHÉSIF STRUCTUREL SANS AFFAISSEMENT À HAUTE RÉSISTANCE EN 2 PARTIES, CARTOUCHE DOUBLE 50 ML, BLANC LAITEUX/TRANSLUCID
- GLD# HEN-100238
- MFG# 398455
- UPC 079340830752
Min. Order Qty 1
Description
Loctite adhésif structurel, sans affaissement de haute résistance en 2 parties, gamme : hysol chaque 608, conteneur à double cartouche, Récipient de 50 ml, base époxy, composition : partie a : silice de résine époxy, amorphe, furieux, sans cristal, léthylène glycol ; partie b : durcisseur polymercaptan, aminophénol substitué, silice, amorphe, furieux, sans cristal, éthylène glycol, 5 min de travail, 15 min de cure fonctionnelle, Durcissement de 24 heures, blanc laiteux/translucide/ambre, 130 deg f, 1 :1 rapport de mélange, <0.4 % voc, à utiliser sur : céramique, métal et plastique
Specifications
| Color | Dark Gray Part A, Gray Part B |
|---|---|
| UNSPSC | 31201601 |
| Application | Abrasion Resistant, Corrosion Protection, Wear Resistant Coatings and Wear-Resistant Coatings |
| Base Type | Epoxy |
| Container Size | 1 lb |
| Flash Point | Part A: > 93 deg C, Part B: 250 deg C |
| Temperature Rating | -30 to 105 deg C |
| Type | 2-Part |
| Composition | Part A: Aluminum Oxide, Diethylenetriamine, Alkyl Phenol, Silicon Dioxide, Epoxy Polyamine Adduct, 4,4'-Isopropylidenediphenol, Triethylenetetramine, Substituted Piperazine, Titanium Dioxide, Aluminum, Alkyl Phenol, Benzyl Alcohol, Benzyldimethylamine ; P |
| Container Type | Kit |
| Curing Time | 6 hr |
| Form | Paste Part A/Solid/Paste Part B |
| Specific Gravity | Part A: 1.07/Part B: 2.228 |
| Series | PC 7222 |
| Application Time | 30 min |
| Coverage | 342 sq-cm at 6 mm THK/0.45 kg |
| Mixing Ratio | 2:1 By Volume/2:1 By Weight |
| Odor/Scent | Part A: Ammoniacal, Part B: Slight/Epoxy |
| Shear Strength | 2440 psi |
| Tensile Strength | 3020 psi |
| Applicable Materials | Aluminum, Brass, Concrete, Iron, Plastic, Steel, Wood |
Features
- Ceramic fibers that give this trowelable putty excellent wear and abrasion resistant properties under typical dry service temperatures of -29 to 107 deg C
- Provides smooth, low friction finish for equipment exposed to wear, erosion, and cavitation
- Renews worn surfaces fast reduces downtime
- Small ceramic bead filled resists fine particle sliding abrasion, prolongs equipment life
- D 89 shore hardness
- 45 to 55 gel time at 25 deg C
- Epoxy hardener part A, epoxy resin part B